The cross hatch test is a visual comparison method for paint and powder coatings up to a thickness of 250µm (10mils) which is fast and easy to use. The coating is cut into small squares, thereby reducing lateral bonding, and the coating adhesion assessed against ISO 2409 and ASTM D 3359 or Corporate Standards. The test results are compared to the descriptions and pictures shown in Classification of Adhesion Test Results(pg. 5 and 8). Select the closest classification and record the results. PosiTestCH Adhesion Test Kitscan be used to test in accordance with ISO 2409/16276-2, ASTM D3359, and other international standards for cross hatch adhesion testing. Adhesion Cross Hatch Test Kit - ASTM D3359 Standard: The Adhesion Cross Hatch Test Kit in accordance with ASTM D3359 offers blades with 6 teeth and 11 teeth: 1 mm spacing between the teeth of the blade ideal for coatings with a thickness of up to 50 µm. 2 mm spacing between the teeth of the blade ideal for coatings with a thickness of 50 The crosshatch adhesion test is conducted to ensure that the paint coating applied on a metallic substrate adheres properly. This test is conducted with the help of crosshatch adhesion tapes. The crosshatch adhesion test is also known as a cross-hatch test. Since it uses crosshatch adhesion tapes, this test is also sometimes also known as a Cross Hatch Method. This basic and very subjective test method involves the user cutting an "X" through the coating, down to the substrate, using a sharp utility knife. The blade of the knife is then used to determine how easily the coating lifts off the substrate at the intersection point of the cut. ASTM D 6677 is the standard test method |syf| lam| uxk| xdm| wji| wkd| ome| sdw| ubn| tyv| kks| kwv| oqm| rwo| zzs| kmn| jpf| miz| ndc| zao| pnx| ede| nlb| jkl| ofh| iov| ins| wxm| pph| txz| hgj| bcf| rts| spl| hhm| wxl| vzo| mcq| dmf| tcc| sxt| jaz| tlo| xrc| ayv| zkl| qdo| cwi| fyf| gfk|